[Titanflash]

I have a very fine Alu 1,5µm and i have German Dark,but the Atomized Alu is better
im not understand why. ?

example

1 gr Flash open with 1,5µm Alu Atomized and KCLO4 20µm


http://www.mitglied.lycos.de/arsch2010/keller.mpg



(with KCLO4 10 µm is the Flash extremely strong)

[Bert]

Titanflash-

Read this immediately (http://www.roguesci.org/theforum/misc.php?s=&action=faq)

And then read this, if you're around long enough. (http://www.roguesci.org/theforum/forumdisplay.php?s=&forumid=16&pagenumber=1&sortfield=lastpost&sortorder=desc&daysprune=1000&x=8&y=12)

Dude, you started a thread for your first post... Also, the link you posted doesn't take me to anything useful. And your post doesn't describe WHAT you made and compared fully enough, nor WHY you think the results different than you would have expected.

That said, salutes can be made with ANY grain geometry of Aluminum if: The grain size is small enough OR the device is large enough or well enough contained. For larger or better contained devices, the denser atomized Al will permit a larger weight of charge per volume than flake Al, therefore you've got more explosive in the device, volume for volume.

Edit your post to add FULL information on your experiment's parameters... And pray that NBK2000 is too busy to notice this!

(Edited to add)
Cut and pasted the URL, saw a video of a small pile of flash being ignited. What good does a view of only one of your experiments do?

[Rhadon]

And then read this, if you're around long enough. He isn't :D.